ABS 韩国LG XR-407E 汽车部件 注塑 电器外壳支架塑胶原料
发布者：上海韬盛塑化科技有限公司 发布时间：2023-02-13 14:04:30 访问次数：17
基本性能额定值单位测试方法
| 融体流动速率 |
|
| ASTM D-1238 |
| (200℃/5kg) | 1 | g/10min |
|
| (220℃/10kg) | 7 | g/10min |
|
| 熔体流动速率 (230℃/3.8kg) | 3 | g/10min | ASTM D-1238 |
物理性能额定值单位测试方法
| 比重 | 1.08 | g/cc | ASTM D-792 |
| 模具收缩率 | 0.4-0.7 | % | ASTM D-955 |
机械性能额定值单位测试方法
| 拉伸屈服强度 (50mm/min) | 450 | kg/cm | ASTM D-638 |
| 拉伸模量 (1mm/min) | 23000 | kg/cm | ASTM D-638 |
| 屈服伸长率 (50mm/min) | 6 | % | ASTM D-638 |
| 断裂伸长率 (50mm/min) | 20 | % | ASTM D-638 |
| 弯曲强度 (15mm/min) | 750 | kg/cm | ASTM D-790 |
| 弯曲模量 (15mm/min) | 25500 | kg/cm | ASTM D-790 |
| IZOD缺口冲击强度 |
|
| ASTM D-256 |
| (1/4" 23℃) | 18 | kg.cm/cm |
|
| (1/4" -30℃) | 8 | kg.cm/cm |
|
| (1/8" 23℃) | 19 | kg.cm/cm |
|
| (1/8" -30℃) | 8 | kg.cm/cm |
|
| 洛氏硬度 | 110 | R-scale | ASTM D-785 |
热性能额定值单位测试方法
| 热变形温度 |
|
| ASTM D-648 |
| (18.5kg/cm 1/4"退火) | 110 | ℃ |
|
| (18.5kg/cm 1/4"未退火) | 105 | ℃ |
|
| (4.6kg/cm1/4" 退火) | 119 | ℃ |
|
| (4.6kg/cm1/4" 未退火) | 114 | ℃ |
|
| 维卡软化点 (5kg, 50℃/h) | 115 | ℃ | ASTM D-1525 |
| 阻燃等级 |
|
| UL94 |
| (1/8") | HB | calss |
|
| (1/16") | HB | calss |
|