| 特性 | 抗撞击性，高 耐热性，高 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Compressive Stress vs. Strain (ASTM D695) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 密度 | 1.22 | g/cm3 | ISO 1183 |
| 溶化体积流率（MVR）(265°C/5.0 kg) | 10.0 | cm3/10min | ISO 1133 |
| 收缩率 - 流动(3.20 mm) | 0.40 到 0.60 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.40 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.10 | % | ISO 62 |
| 拉伸模量 | 3200 | MPa | ISO 527-2/1 |
| 拉伸应力 | ISO 527-2/5 | ||
| 屈服 | 55.0 | MPa | ISO 527-2/5 |
| 断裂 | 58.0 | MPa | ISO 527-2/5 |
| 拉伸应变 | ISO 527-2/5 | ||
| 屈服 | 4.2 | % | ISO 527-2/5 |
| 断裂 | 100 | % | ISO 527-2/5 |
| 弯曲模量1 | 3100 | MPa | ISO 178 |
| 弯曲应力 | 95.0 | MPa | ISO 178 |
| 简支梁缺口冲击强度2(23°C) | 35 | kJ/m2 | ISO 179/1eA |
| 悬壁梁缺口冲击强度3 | ISO 180/1A | ||
| -30°C | 10 | kJ/m2 | ISO 180/1A |
| 23°C | 30 | kJ/m2 | ISO 180/1A |
| 热变形温度4(1.8 MPa, 未退火, 64.0 mm跨距) | 118 | °C | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 135 | °C | ISO 306/B50 |
| -- | 137 | °C | ISO 306/B120 |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 : -40 到 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 : -40 到 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| 干燥温度 | 110 到 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，大 | 8.0 | hr | |
| 建议的大水分含量 | 0.040 | % | |
| 建议注射量 | 30 到 80 | % | |
| 料筒后部温度 | 260 到 271 | °C | |
| 料筒中部温度 | 266 到 288 | °C | |
| 料筒前部温度 | 271 到 299 | °C | |
| 射嘴温度 | 271 到 299 | °C | |
| 加工（熔体）温度 | 282 到 299 | °C | |
| 模具温度 | 77 到 99 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.038 到 0.076 | mm |