| 熔体流动速率 | |||
| 30 | g/10min | ASTM D1238 | |
| (190℃/2.16kg) | 30 | g/10min | ISO 1133 |
| 吸水率 (24 hr) | 0.2 | % | ASTM D570 |
| 比重 | 1.41 | g/cm | ASTM D792,ISO 1183 |
| 成型收缩率 | |||
| (Flow) | 1.5-1.9 | % | ASTM D955 |
| (Across Flow) | 1.6-2 | % | ISO 294-4 |
| (Flow) | 1.6-2 | % | ISO 294-4 |
| 洛氏硬度 | ASTM D785 | ||
| (M-Scale) | 80 | ||
| (R-Scale) | 115 |
| 拉伸模量 | 2850 | MPa | ISO 527-2 |
| 屈服拉伸应力 | 66 | MPa | ISO 527-2 |
| 拉伸应力 | 60 | MPa | ASTM D638 |
| 断裂伸长率 | |||
| 50 | % | ASTM D638 | |
| 30 | % | ISO 527-2 | |
| 弯曲模量 | 2630 | MPa | ASTM D790 |
| 弯曲强度 | 90 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles) | 14 | mg | ASTM D1044 |
| CHARPY缺口冲击强度 (23℃) | 4 | kJ/m | ISO 179/1eA |
| Izod 缺口冲强度 | 39 | J/m | ASTM D256 |
| 热变形温度 | |||
| (0.45MPa,unannealed) | 158 | ℃ | ASTM D648 |
| (0.45MPa,unannealed) | 157 | ℃ | ISO 75-2/B |
| (1.8MPa,unannealed) | 110 | ℃ | ASTM D648 |
| (1.8MPa,unannealed) | 100 | ℃ | ISO 75-2/A |
| 流动方向线性热膨胀系数 | 0.0001 | cm/cm/℃ | ASTM E831 |
| 阻燃等级 | HB | UL 94 |