| 24小时吸水率 | 5 | % | ASTM D-570 |
| 熔体流动速率 | 10 | g/10min | ASTM D-1238 |
| 泰伯磨耗量 | ASTM D-1044 | ||
| (H 18轮) | 310 | mg/1000rev | |
| (CS-17轮) | 30 | mg/1000rev | |
| 比重 | 1.15 | ASTM D-792 |
| 断裂伸长 | 200 | % | ASTM D-638 |
| 硬度计硬度 | 35 | ASTM D-2240 | |
| 断裂拉伸力 | 10.3 | Mpa | ASTM D-638 |
| 初耐撕裂性能 | 51 | kn/m | ASTM D-1004 |
| 揉曲模量 (23℃) | 32.4 | Mpa | ASTM D-790 |
| 拉伸力 | ASTM D-638 | ||
| 1.7 | Mpa | ||
| 2.6 | Mpa | ||
| 埃佐冲击强度 (23℃) | 不破裂 | J/m | ASTM D-256 |
| 维卡软化点 | 77 | ℃ | ASTM D-1525 |
| 熔点 | 156 | ℃ | ASTM D-3418 |
| 热畸变温度 | ASTM D-648 | ||
| (@0.5Mpa) | N/A | ℃ | |
| (@0.18Mpa) | N/A | ℃ |
| 耐揉曲切口增长性能 | >1×10 |